| About |
|---|
| LOTADER® LX4110 is a random terpolymer of ethylene, acrylic ester and maleic anhydride, polymerized by high-pressure autoclave process. Applications LOTADER® LX4110 is a versatile adhesive for extrusion coating or lamination, designed as: Concentrate to be used in dry blend with LDPE. LOTADER® LX4110 improves adhesion of LDPE on aluminium foils, metallized or primerized films. Ready for use resin to be used pure. LOTADER® LX4110 gives excellent adhesion on substrates likes aluminium foil, metallized plastics, paper, board, PE and some plastic films like BOPP.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | EAA |
| Material Status | Commercial: Active |
| Features | Low shrinkage,Good bond,High pressure heat resistance,Terpolymer,Heat Stabilized,Higher melt stability |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.940 | g/cm³ | ASTM D1505 |
| Density | 0.940 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 5.0 | g/10min | ASTM D1238 |
| 190℃，2.16kg | 5.0 | g/10min | ISO 1133 |
| Ethyl acrylate content | 5.0 | wt% | |
| Maleic anhydride content | 3.0 | wt% | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds, molded | 46 | ISO 868 | |
| Shore D, 15 seconds, molded | 46 | ASTM D2240 | |
| tensile strength | |||
| Fracture, molded | 11.0 | MPa | ASTM D638 |
| Fracture, molded | 11.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, molded | 650 | % | ISO 527-2 |
| Fracture, molded | 650 | % | ASTM D638 |
| Bending modulus | |||
| Compression Molding | 140 | MPa | ISO 178 |
| Compression Molding | 140 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 78.0 | ℃ | ASTM D1525 2 |
| Vicat Softening Temp | 78.0 | ℃ | ISO 306/A |
| Melting temperature | 105 | ℃ | ISO 11357-3 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |