| About |
|---|
| LOTADER® TX8030 is a random terpolymer of ethylene, acrylic ester and maleic anhydride, polymerized by high-pressure autoclave process. LOTADER® TX8030 is a versatile adhesive for extrusion coating or lamination, designed as: Concentrate to be used in dry blend with LDPE. LOTADER® TX8030 improves adhesion of LDPE on aluminium foils, metallized or primerized films. Ready for use resin to be used pure. LOTADER® TX8030 gives excellent adhesion on substrates likes aluminium foil, metallized plastics, paper, board, PE and its copolymers. Coextrusion tie layer for PE/PA in extrusion coating process.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | EEA |
| Material Status | Commercial: Active |
| Features | Good dissection,Good bond,Terpolymer,Heat Stabilized,Higher melt stability |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.940 | g/cm³ | ASTM D1505 |
| Density | 0.940 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 3.0 | g/10min | ASTM D1238 |
| 190℃，2.16kg | 3.0 | g/10min | ISO 1133 |
| Ethyl acrylate content | 13.0 | wt% | |
| Maleic anhydride content | 2.8 | wt% | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 36 | ISO 868 | |
| Shaw’s D, molded | 36 | ASTM D2240 | |
| tensile strength | |||
| Fracture, molded | 12.0 | MPa | ISO 527-2 |
| Fracture, molded | 12.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, molded | 700 | % | ASTM D638 |
| Fracture, molded | 700 | % | ISO 527-2 |
| Bending modulus | |||
| Compression Molding | 130 | MPa | ASTM D790 |
| Compression Molding | 130 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 65.0 | ℃ | ASTM D1525 2 |
| Vicat Softening Temp | 65.0 | ℃ | ISO 306/A |
| Melting temperature | 95.0 | ℃ | ISO 11357-3 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |