| About |
|---|
| Lotrène® Q2018 Series are Linear Low Density Polyethylene resins produced in a gas phase reactor using butene (C4) co-monomer. They are designed for blown film applications and can be used in pure form as well as blended with other PE resins, such as LDPE or HDPE and mPE resins for mono extrusion or co-extrusion process to modify film properties. Lotrène® Q2018 Series are suited for many applications in the field of consumer, industrial, food or hygiene packaging such as freezer film, bread bags, shoppers and bags as well as lamination film and multilayer packaging film.&& |
| Product Description | |
|---|---|
| Supplier | QAPCO |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Smoothness,High anti-blocking,Butylene copolymer,Heat Stabilized |
| Availabilitys | Africa & Middle East ,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.918 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus | ASTM D882 | ||
| 1% secant, MD: 40 µ m, blow molded film | 215 | MPa | ASTM D882 |
| 1% secant, TD: 40 µ m, blow molded film | 245 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield, 40 µ m, blow molded film | 11.0 | MPa | ASTM D882 |
| TD, yield, 40 µ m, blow molded film | 11.0 | MPa | ASTM D882 |
| MD, fracture, 40 µ m, blow molded film | 35.0 | MPa | ASTM D882 |
| TD, fracture, 40 µ m, blow molded film | 32.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 40 µ m, blow molded film | 850 | % | ASTM D882 |
| TD, fracture, 40 µ m, blow molded film | 900 | % | ASTM D882 |
| Drop hammer impact | |||
| 40 µ m, blow molded film | 130 | g | ASTM D1709 |
| Elmandorf tear strength | ASTM D1922 | ||
| MD: 40 µ m, blow molded film | 220 | g | ASTM D1922 |
| TD: 40 µ m, blow molded film | 420 | g | ASTM D1922 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 100 | ℃ | ASTM D1525 |
| Crystallization peak temperature | |||
| DSC | 121 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 40.0 µ m, blow molded film | 55 | ASTM D2457 | |
| Haze | |||
| 40 µ m, blow molded film | 14 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 170 to 210 | °C | |
| Barrel 2 zone temperature | 170 to 210 | °C | |
| Barrel 3 zone temperature | 170 to 210 | °C | |
| Barrel 4 zone temperature | 170 to 210 | °C | |
| Barrel 5 zone temperature | 170 to 210 | °C | |
| Melt temperature | 190 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. F50 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |