LOTRYL® 17BA07N is a random copolymer of Ethylene and Butyl Acrylate produced by high-pressure radicalar polymerization process. Applications LOTRYL® 17BA07N grade thanks to the production process and the continuous quality control is polymer of choice to produce internal and external fully bonded shields for electrical cables. The process ensures unmatched polymer distribution, good carbon black dispersion, high thermal stability during extrusion and along cables use; then it extends the cable service duration. LOTRYL® 17BA07N withstand the more stringent cross-inking conditions.&&

About

LOTRYL® 17BA07N is a random copolymer of Ethylene and Butyl Acrylate produced by high-pressure radicalar polymerization process. Applications LOTRYL® 17BA07N grade thanks to the production process and the continuous quality control is polymer of choice to produce internal and external fully bonded shields for electrical cables. The process ensures unmatched polymer distribution, good carbon black dispersion, high thermal stability during extrusion and along cables use; then it extends the cable service duration. LOTRYL® 17BA07N withstand the more stringent cross-inking conditions.&&

Product Description
Supplier	Arkema
Generic	EBA
Material Status	Commercial: Active
Features	Random copolymer,Heat Stabilized
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.930	g/cm³	ASTM D1505
Density	0.930	g/cm³	ISO 1183
Melt Flow Rate
190℃，2.16kg	6.2 to 8.3	g/10min	ASTM D1238
190℃，2.16kg	6.2 to 8.3	g/10min	ISO 1133
Butyl acrylate composition	15.0 to 19.0	wt%

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	30		ISO 868
Shaw’s D	30		ASTM D2240
tensile strength
fracture	15.0	MPa	ASTM D638
fracture	15.0	MPa	ISO 527-2
Tensile strain
fracture	700	%	ASTM D638
fracture	700	%	ISO 527-2
Bending modulus	40.0	MPa	ASTM D790
Bending modulus	40.0	MPa	ISO 178

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	58.0	℃	ASTM D1525 2
Vicat Softening Temp	58.0	℃	ISO 306/A
Melting temperature	93.0	℃	ISO 11357-3

Process Conditions
Extrusion	Nominal value	Unit	Test method
Barrel 1 zone temperature	150 to 170	°C
Barrel 2 zone temperature	170	°C
Barrel 3 zone temperature	170	°C
Barrel 4 zone temperature	170	°C
Nozzle temperature	170	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.