| About |
|---|
| XL510H resin is produced by ExxonMobil Chemicalu0027s autoclave process technology. And XL510H resin is a product designed for low Neck-In, Good adhesion to a variety of substance. |
| Product Description | |
|---|---|
| Supplier | LOTTE |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Low shrinkage,Good bond,Low density |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 5.5 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Oxygen permeability | 200 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water vapor transmittance (38 ° C, 90% RH, 25 µ m) | 19 | g/m²/24 hr | ASTM F372 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 88.0 | ℃ | ASTM D1525 |
| Melting temperature | 106 | ℃ | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| extrusion | Nominal value | Unit | Test method |
| Maximum Coating Speed | 6.7 | m/sec | Internal Method |
| Minimum Coating Weight – Constant output (315 ° C) | 10.0 | g/m² | Internal Method |
| Internal shrinkage – Constant output, 150 m/min (315 ° C) | 30.0 | mm | Internal Method |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |