| Resin of LTP PL serials is pure PPS resin with high density and molecular weight. Modified reinforced materials and coating materials can be produced base on this kind of resin&& |
| Product Description | |
|---|---|
| Supplier | Letian |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | High molecular weight,High density |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.34 to 1.36 | g/cm³ | GB/T 1033 |
| Melt Flow Rate | 25 to 700 | g/10min | GB/T 3682 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.50 | % | GB/T 1034 |
| Ash Content | 0.15 | % | GB/T 9345 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 90.0 | MPa | GB/T 1040 |
| Tensile strain | |||
| fracture | 20 | % | GB/T 1040 |
| bending strength | 100 | MPa | GB/T 1042 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 12 | kJ/m² | GB/T 1043 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 290 | ℃ | GB/T 4608 |
| Hot deformation temperature | 110 | ℃ | GB/T 1634 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+16 | ohms | GB/T 1410 |
| Volume resistivity | 1.0E+15 | ohms·cm | GB/T 1410 |
| Dielectric constant | GB/T 1409 | ||
| 1 kHz | 3.00 | GB/T 1409 | |
| 1 MHz | 3.00 | GB/T 1409 | |
| Dissipation factor | GB/T 1409 | ||
| 1 kHz | 6.0E-4 | GB/T 1409 | |
| 1 MHz | 1.5E-3 | GB/T 1409 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |