| Compound based on PA66 natural first choice. Lubricated and nucleated.&& |
| Product Description | |
|---|---|
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Nucleation,Lubricating,V-2 |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.11 to 1.15 | g/cm³ | ISO 1183/A |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2500 to 3000 | MPa | ISO 527-2/1A/1 |
| tensile strength | ISO 527-2/1A/50 | ||
| yield | 60.0 to 65.0 | MPa | ISO 527-2/1A/50 |
| fracture | 60.0 to 65.0 | MPa | ISO 527-2/1A/50 |
| Tensile strain | ISO 527-2/1A/50 | ||
| yield | 5.0 to 8.0 | % | ISO 527-2/1A/50 |
| fracture | 5.0 to 8.0 | % | ISO 527-2/1A/50 |
| Bending modulus | 1800 to 2300 | MPa | ISO 178 |
| bending strength | 65.0 to 70.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 2.5 to 4.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 40 to 60 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 30 to 50 | J/m | ASTM D256-A |
| 23℃ | 80 to 90 | kJ/m² | ASTM D256 |
| 23℃ | 3.0 to 5.0 | kJ/m² | ASTM D256 |
| 23℃ | 2.5 to 4.5 | kJ/m² | ISO 180-A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 50 to 70 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 215 to 225 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 220 to 230 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed, 3.2 mm | 70.0 to 80.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| — | 240 to 250 | ℃ | ISO 306/A120 |
| B120 | 230 to 240 | ℃ | ISO 306/B120 |
| Melting temperature | 250 to 265 | ℃ | Internal Method |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.20 mm | V-2 | UL 94 | |
| Glowing wire flammability index | |||
| 2.0 mm | 850 | ℃ | IEC 60695-2-12 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. Notch E |
| 4. Notch A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |