| About |
|---|
| Compound based on blend PC/ABS second choice. Black coloured.&& |
| Product Description | |
|---|---|
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 to 1.17 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 260℃，5.0kg | 15 to 20 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2000 to 2500 | MPa | ISO 527-2/1A/1 |
| tensile strength | ISO 527-2/1A/50 | ||
| yield | 50.0 to 55.0 | MPa | ISO 527-2/1A/50 |
| fracture | 45.0 to 50.0 | MPa | ISO 527-2/1A/50 |
| Tensile strain | ISO 527-2/1A/50 | ||
| yield | 6.0 to 8.0 | % | ISO 527-2/1A/50 |
| fracture | 45 to 50 | % | ISO 527-2/1A/50 |
| Bending modulus | 1800 to 2300 | MPa | ISO 178 |
| bending strength | 55.0 to 60.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 40 to 45 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 无断裂 | ISO 179/1eU | |
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 450 to 500 | J/m | ASTM D256-A |
| 23℃ | 无断裂 | ASTM D256 | |
| 23℃ | 45 to 50 | kJ/m² | ASTM D256 |
| 23℃ | 40 to 45 | kJ/m² | ISO 180-A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 无断裂 | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 115 to 125 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 120 to 130 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed, 3.2 mm | 100 to 110 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| — | 125 to 135 | ℃ | ISO 306/A120 |
| B120 | 120 to 130 | ℃ | ISO 306/B120 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. Notch E |
| 4. Notch A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |