| Compound based on PP first choice natural. With glass beads 40%.&& |
| Product Description | |
|---|---|
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 to 1.24 | g/cm³ | ISO 1183/A |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2200 to 3200 | MPa | ISO 527-2/1A/1 |
| tensile strength | ISO 527-2/1A/5 | ||
| yield | 25.0 to 30.0 | MPa | ISO 527-2/1A/5 |
| fracture | 20.0 to 25.0 | MPa | ISO 527-2/1A/5 |
| Tensile strain | ISO 527-2/1A/5 | ||
| yield | 4.0 to 5.0 | % | ISO 527-2/1A/5 |
| fracture | 25 to 30 | % | ISO 527-2/1A/5 |
| Bending modulus | 1700 to 2700 | MPa | ISO 178 |
| bending strength | 35.0 to 45.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 3.5 to 4.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 25 to 35 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 30 to 40 | J/m | ASTM D256-A |
| 23℃ | 25 to 35 | kJ/m² | ASTM D256 |
| 23℃ | 3.0 to 4.0 | kJ/m² | ASTM D256 |
| 23℃ | 3.5 to 4.5 | kJ/m² | ISO 180-A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 25 to 35 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 120 to 130 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 125 to 135 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed, 3.2 mm | 60.0 to 70.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| — | 100 to 110 | ℃ | ISO 306/A120 |
| B120 | 95.0 to 105 | ℃ | ISO 306/B120 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. Notch E |
| 4. Notch A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |