| PolyOne’s LubriOne TM Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating, offering low coefficient of friction and improved wear resistance properties. These compounds combine the unique benefits of internal lubricants such PTFE, silicone, Aramide and molybdenum disulfide with a wide array of reinforcements and base engineering resins. Available in a wide range of physical properties, these materials are specified where certain key performance issues are critical. In addition to the standard range, products can be custom-formulated to meet your specific requirements or colors, offering you both product and design flexibility.&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | Copolymer Polyformaldehyde |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Low coefficient of friction,Lubricating,Good wear resistance |
| Availabilitys | Africa & Middle East ,North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.42 | g/cm³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 8800 | MPa | ISO 527-2 |
| tensile strength | 50.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 0.50 to 1.0 | % | ISO 527-2 |
| Bending modulus | 5500 | MPa | ISO 178 |
| bending strength | 65.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.0 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | 12 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 120 | ℃ | ISO 75-2/A |
| Melting temperature | |||
| DSC | 165 to 170 | ℃ | ISO 3146 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.20 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 100 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Processing (melt) temperature | 190 to 210 | °C | |
| Mold temperature | 75 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. +/-0.02 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |