| About |
|---|
| Carbon Fiber, PTFE and Graphite Filled High Flow PEEK Compound&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | PEEK |
| Material Status | Commercial: Active |
| Features | Low coefficient of friction,High Heat Resistance,Lubricating,Good wear resistance,V-0 |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.43 | g/cm³ | ISO 1183 |
| Shrinkage rate | ASTM D955 | ||
| MD：23℃，3.2 mm | 0.10 to 0.30 | % | ASTM D955 |
| TD：23℃，3.2 mm | 1.5 to 1.7 | % | ASTM D955 |
| Water absorption rate | ASTM D570 | ||
| 23℃，24hr | 0.040 | % | ASTM D570 |
| Saturation, 23 ℃ | 0.10 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 6.0 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| 23℃ | 35 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 315 | ℃ | ASTM D648 |
| Glass transition temperature | 145 | ℃ | DSC |
| Melting temperature | 343 | ℃ | DSC |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD：< 143℃ | 1.2E-5 | 1/℃ | ISO 11359-2 |
| MD：> 143℃ | 1.3E-5 | 1/℃ | ISO 11359-2 |
| TD：< 143℃ | 7.5E-5 | 1/℃ | ISO 11359-2 |
| TD：> 143℃ | 2.2E-4 | 1/℃ | ISO 11359-2 |
| Thermal conductivity coefficient | ASTM C177 | ||
| 60℃ | 0.46 | W/m/K | ASTM C177 |
| 60℃ | 1.4 | W/m/K | ASTM C177 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+10 to 1.0E+13 | ohms | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | V-0 | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 84 | ISO 868 | |
| Tensile modulus | |||
| 23℃，3.20 mm | 12000 | MPa | ISO 527-2/1/5 |
| tensile strength | ISO 527-2/1/5 | ||
| Fracture, 23 ℃, 3.20 mm | 155 | MPa | ISO 527-2/1/5 |
| Fracture, 120 ℃, 3.20 mm | 115 | MPa | ISO 527-2/1/5 |
| Tensile strain | |||
| Fracture, 23 ℃, 3.20 mm | 2.0 | % | ISO 527-2/1/5 |
| Bending modulus | ASTM D790 | ||
| 23℃，3.20 mm | 12000 | MPa | ASTM D790 |
| 120℃，3.20 mm | 11500 | MPa | ASTM D790 |
| bending strength | ASTM D790 | ||
| Fracture, 23 ℃, 3.20 mm | 225 | MPa | ASTM D790 |
| Fracture, 120 ℃, 3.20 mm | 185 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 150 to 160 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Processing (melt) temperature | 350 to 390 | °C | |
| Mold temperature | 180 to 200 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. ±0.03 |
| 3. 0.051 in/min |
| 4. through-plane |
| 5. in-plane |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |