| About |
|---|
| LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability.&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Low coefficient of friction,Lubricating,Good wear resistance |
| Availabilitys | Africa & Middle East ,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.26 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr，3.18 mm | 0.15 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1590 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 60.7 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 10 to 12 | % | ASTM D638 |
| Bending modulus | 1590 | MPa | ASTM D790 |
| bending strength | 64.8 | MPa | ASTM D790 |
| friction coefficient | ASTM D1894 | ||
| Steel – Dynamic | 0.40 | ASTM D1894 | |
| Steel – Static | 0.25 | ASTM D1894 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 130 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.35 mm | 127 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.35 mm | 121 | ℃ | ASTM D648 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 288 to 316 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 0.20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |