| About |
|---|
| Applications General purpose thermoplastic elastomer for polymer modification Shoe sole, Wire & Cable, Packaging Films Description LUCENE™ LC180 is an ethylene-1-octene copolymer produced using LG Chem’s metallocene polymerization catalyst and solution process technology. LUCENE™ LC180 is an excellent impact modifier for plastics and offers unique performance capabilities for compounded products.&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Active |
| Features | Good Clarity,Good tear strength,Copolymer |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.885 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.2 | g/10min | ASTM D1238 |
| Mooney viscosity | |||
| ML 1+4，121℃ | 20 | MU | ASTM D1646 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | 58.0 | kN/m | ASTM D624 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | -45.0 | ℃ | Internal Method |
| Melting temperature | |||
| DSC | 73.0 | ℃ | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 86 | ASTM D2240 | |
| tensile strength | |||
| fracture | 28.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 800 | % | ASTM D638 |
| Bending modulus | |||
| 1% secant | 30.0 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 7.9 in/min |
| 3. 20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |