| About |
|---|
| LUCENE™ LF100 is an ethylene-1-octene copolymer produced using LG Chem’s metallocene polymerization catalyst and solution process technology. LUCENE™ LF100 is mainly intended for the extrusion of blown film with high mechanical property for the manufacture of lamination and packaging film. LUCENE™ LF100 does contain Slip agent and Anti-block agent. LUCENE™ LF100 complies with FDA regulation 21 CFR 177.1520(c)(3.2c). Applications General purpose thermoplastic elastomer for polymer modification Lamination film, Packaging Film&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Active |
| Features | Smoothness,High anti-blocking,Octene copolymer |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.902 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.2 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 91 | ASTM D2240 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| MD, fracture | 45.0 | MPa | |
| TD, fracture | 48.0 | MPa | |
| Tensile strain | |||
| MD, fracture | 570 | % | |
| TD, fracture | 650 | % | |
| tear strength | |||
| MD | 60.8 | kN/m | |
| TD | 169.7 | kN/m |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | -35.0 | ℃ | Internal Method |
| Melting temperature | 92.0 | ℃ |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | 7.0 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |