| About |
|---|
| Lucky Enpla LAY7000是一种丙烯腈丁二烯苯乙烯 + 丙烯酸 (PMMA)（ABS + 丙烯酸）产品,。 它可以通过注射成型进行加工,在北美洲、欧洲或亚太地区有供货。 典型应用领域为:电气/电子应用。 主要特性为:高光泽度。&& |
| Product Description | |
|---|---|
| Supplier | Lucky Enpla |
| Generic | ABS+PMMA |
| Material Status | Commercial: Active |
| Features | Good surface appearance,Good liquidity |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.12 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 27 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 to 0.70 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 53.9 | MPa | ASTM D638 |
| Bending modulus | 2450 | MPa | ASTM D790 |
| bending strength | 76.5 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | ASTM D256 | ||
| 3.2 mm | 110 | J/m | ASTM D256 |
| 6.4 mm | 98 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 83.0 | ℃ | ASTM D648 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 70 to 90 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Barrel rear temperature | 210 to 230 | °C | |
| Barrel middle temperature | 220 to 240 | °C | |
| Barrel front temperature | 220 to 240 | °C | |
| Nozzle temperature | 220 to 240 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Back pressure | 1.96 to 3.92 | MPa | |
| Screw speed | 60 to 80 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |