| About |
|---|
| Description Flame Retardant Applications Connectors&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,V-0 |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.50 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 to 0.90 | % | ASTM D955 |
| Water absorption rate | |||
| balance | 0.70 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 59 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 190 | ℃ | ASTM D648 |
| Melting peak temperature | 220 | ℃ | ASTM D3418 |
| 0.75 mm | 115 | ℃ | UL 746 |
| 1.5 mm | 115 | ℃ | UL 746 |
| 3.0 mm | 115 | ℃ | UL 746 |
| Relative temperature index | |||
| Electrical performance | UL 746 | ||
| Strength mechanical performance | UL 746 | ||
| Impact mechanical performance | UL 746 | ||
| 0.75 mm | 110 | ℃ | UL 746 |
| 1.5 mm | 110 | ℃ | UL 746 |
| 3.0 mm | 110 | ℃ | UL 746 |
| 0.75 mm | 120 | ℃ | UL 746 |
| 1.5 mm | 120 | ℃ | UL 746 |
| 3.0 mm | 120 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 23℃ | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 23 ℃，1 mm | 21 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 23 ℃，1 MHz | 3.80 | ASTM D150 | |
| Arc resistance | 90.0 | sec | ASTM D495 |
| Compared to the leakage tracing index | |||
| Solution A | 250 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.75 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 5VA | UL 94 | |
| 3.00 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, 3.20 mm | 118 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm | 2.8 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm | 5980 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 3.20 mm | 157 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 120 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 100 | °C | |
| Drying time | 4.0 to 5.0 | hr | |
| Barrel rear temperature | 240 to 260 | °C | |
| Barrel middle temperature | 245 to 265 | °C | |
| Barrel front temperature | 250 to 270 | °C | |
| Nozzle temperature | 255 to 270 | °C | |
| Processing (melt) temperature | 255 to 270 | °C | |
| Mold temperature | 80 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. 0.051 in/min |
| 4. 23°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |