| About |
|---|
| Description General Purpose Applications Automotive(Air Intake Manifold, Cylinder Head Cover)&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.38 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.4-0.9 | % | ASTM D995 |
| Water absorption rate | |||
| 23℃，24hr | 0.7 | % | ASTM D570 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 260 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 250 | ℃ | ASTM D648 |
| Melting temperature | 260 | ℃ | ASTM D3418 |
| Vicat Softening Temp | |||
| Linear coefficient of thermal expansion | |||
| MD | 3 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 1.0E+14 | Ω.cm | ASTM D257 |
| Insulation strength | |||
| 25 | KV/mm | ASTM D149 | |
| Dielectric constant | |||
| 4 | 1 MHz | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75mm | HB | UL-94 | |
| 1.50mm | HB | UL-94 | |
| 3.00mm | HB | UL-94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 130 | J/m | ASTM D256 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 122 | R 级 | ASTM D785 |
| tensile strength | |||
| 23℃ | 191 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3 | % | ASTM D638 |
| bending strength | |||
| 23℃ | 279 | MPa | ASTM D790 |
| Bending modulus | |||
| 23℃ | 9319 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 -100 | °C | |
| Drying time | 4-5 | Hr | |
| Water content | 0.12 | % | |
| Injection temperature | |||
| Rear barrel temperature | 260-270 | °C | |
| Central temperature of the barrel | 270-285 | °C | |
| Barrel front temperature | 270-290 | °C | |
| Die temperature | 270-295 | °C | |
| Mold temperature | 80-110 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. 0.051 in/min |
| 4. Hydraulic Type |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |