| About |
|---|
| Description General Purpose Applications E&E(Rice Cooer Housing)&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.23 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.90 to 1.3 | % | ASTM D955 |
| Water absorption rate | |||
| balance | 1.3 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 39 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 95.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 6.4 mm | 205 | ℃ | ASTM D648 |
| Melting peak temperature | 220 | ℃ | ASTM D3418 |
| Linear coefficient of thermal expansion | |||
| MD | 5.7E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 23℃ | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 23 ℃，1 mm | 22 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 23 ℃，1 MHz | 4.00 | ASTM D150 | |
| Arc resistance | 185 | sec | ASTM D495 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile strain | |||
| Fracture, 3.20 mm | 6.0 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm | 3630 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 3.20 mm | 108 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 121 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 100 | °C | |
| Drying time | 4.0 to 5.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Barrel rear temperature | 230 to 255 | °C | |
| Barrel middle temperature | 245 to 260 | °C | |
| Barrel front temperature | 245 to 270 | °C | |
| Nozzle temperature | 250 to 270 | °C | |
| Processing (melt) temperature | 250 to 270 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Back pressure 5 | 10.0 to 30.0 | MPa | |
| Screw speed | 60 to 150 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |