| About |
|---|
| Lumid® HI5001AH is a Polyamide + Polyolefin (Nylon+Olefin) material. It is available in Asia Pacific, Europe, Latin America, or North America for blow molding or injection molding. Important attributes of Lumid® HI5001AH are: Chemical Resistant Impact Resistant Typical application of Lumid® HI5001AH: Automotive&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | PA + Olefins |
| Material Status | Commercial: Active |
| Features | High impact resistance,Good melt strength,Block resin,Solvent resistance |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 260℃，12.5kg | 3.0 | g/10min | ASTM D1238 |
| Water absorption rate | |||
| 23℃，24hr | 0.50 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, 3.20 mm | 53.9 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm | 320 | % | ASTM D638 |
| Bending modulus | |||
| 6.40 mm | 1320 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 6.40 mm | 48.1 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -40℃，6.4mm | 250 | J/m | ASTM D256 |
| 23℃，6.4mm | No Break | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting peak temperature | 220 | ℃ | ASTM D3418 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 70 to 90 | °C | |
| Drying time | 4.0 to 5.0 | hr | |
| Barrel rear temperature | 235 to 250 | °C | |
| Barrel middle temperature | 240 to 260 | °C | |
| Barrel front temperature | 240 to 260 | °C | |
| Nozzle temperature | 250 to 265 | °C | |
| Processing (melt) temperature | 250 to 265 | °C | |
| Mold temperature | 80 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.39 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |