| About |
|---|
| Injection Molding Grade, General Purpose Description GF 20% Reinforced, NSF Certified for KA02 and E2035, High Flow, High Impact Strength, Hydrolytic Stability Application Electric and Electronic Parts, Part for Water contact, Water Pump Housing or Impellers&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | High impact resistance,High liquidity,Hydrolysis stability,HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.18 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 280℃，5.0kg | 9.5 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.20 to 0.50 | % | Internal Method |
| Water absorption rate | |||
| 23℃，24hr | 0.060 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 110 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃，3.2 mm | 450 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 140 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.80 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 | |
| 2.50 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 3.20 mm | 95.1 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm | 7.0 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm | 4900 | MPa | ASTM D790 |
| bending strength | |||
| Fracture, 3.20 mm | 137 | MPa | ASTM D790 |
| Rockwell hardness | |||
| Level L | 112 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 100 | °C | |
| Drying time | 4.0 to 5.0 | hr | |
| Recommended maximum moisture content | > 0.030 | % | |
| Barrel rear temperature | 260 to 300 | °C | |
| Barrel middle temperature | 270 to 310 | °C | |
| Barrel front temperature | 270 to 310 | °C | |
| Nozzle temperature | 270 to 310 | °C | |
| Processing (melt) temperature | 280 to 320 | °C | |
| Mold temperature | 70 to 110 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.39 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |