| About |
|---|
| PLA is a biobased polymer derived from natural resources and offers a significant reduction in carbon footprint compared to oil-based plastics. Luminy LX130U is a medium viscosity, medium flow, amorphous, transparent PLA resin suitable for injection molding and fiber spinning.&& |
| Product Description | |
|---|---|
| Generic | PLA |
| Material Status | Commercial: Active |
| Features | Renewable resources,Food contact compliance,Compostable,Moderate liquidity,Amorphous |
| Availabilitys | North America,Latin America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.24 | g/cm³ | |
| Melt Flow Rate | |||
| 190℃，2.16kg | 7.0 | g/10min | |
| 210℃，2.16kg | 14 | g/10min | |
| water content | < 400 | ppm | Karl Fisher |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3500 | MPa | ISO 527-2 |
| tensile strength | 45.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | < 5.0 | % | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | < 5.0 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 55.0 to 60.0 | ℃ | ISO 75-2/B |
| Glass transition temperature | 55.0 to 60.0 | ℃ | DSC |
| Melting temperature | 145 to 160 | ℃ | DSC |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Yellowness index | < 35 | YI |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Monomer Residue | < 0.30 | % | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 85 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Dew Point | < -40 | °C | |
| Recommended maximum moisture content | 0.025 | % | |
| Hopper temperature | 20 to 40 | °C | |
| Barrel rear temperature | 155 to 175 | °C | |
| Barrel middle temperature | 180 to 220 | °C | |
| Barrel front temperature | 180 to 220 | °C | |
| Nozzle temperature | 180 to 220 | °C | |
| Processing (melt) temperature | 180 to 220 | °C | |
| Back pressure | 5.00 to 10.0 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Procedure A |
| 3. Amorphous |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |