| About |
|---|
| Lupol® GP1007FH是一种聚丙烯材料,。 该产品在北美洲、拉丁美洲、欧洲或亚太地区有供货,加工方式为:注射成型。 Lupol® GP1007F的主要特性有: 阻燃/额定火焰 Flame Retardant 典型应用领域包括: 电气/电子应用 汽车行业&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,V-0 |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.940 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 11 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 1.6 to 1.8 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 3.20 mm | 31 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm | 100 | % | ASTM D638 |
| Bending modulus | |||
| 6.40 mm | 1373.4 | MPa | ASTM D790 |
| bending strength | |||
| 6.40 mm | 39.24 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 88 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 6.4 mm | 105 | ℃ | ASTM D648 |
| Relative temperature index | |||
| Electrical performance | 120 | ℃ | UL 746 |
| Strength mechanical performance | 120 | ℃ | UL 746 |
| Impact mechanical performance | 120 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 70 to 80 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Minimum Moisture Content | 0.010 | % | |
| Temperature at the rear of the barrel | 190 to 210 | °C | |
| Temperature in the middle of the barrel | 200 to 230 | °C | |
| Front temperature of material barrel | 200 to 230 | °C | |
| Nozzle temperature | 210 to 230 | °C | |
| Processing (melt) temperature | 200 to 230 | °C | |
| Mold temperature | 40 to 60 | °C | |
| Back pressure | 29.4 to 58.8 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |