| About |
|---|
| Description Low Warpage Application Electrical & Electronic, Automotive Parts&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Low warping,HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.21 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 11 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.30 to 0.50 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 68.6 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 5.0 | % | ASTM D638 |
| Bending modulus | 5490 | MPa | ASTM D790 |
| bending strength | |||
| yield | 98.1 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 120 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 150 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 70 to 90 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Barrel rear temperature | 200 to 220 | °C | |
| Barrel middle temperature | 200 to 230 | °C | |
| Barrel front temperature | 210 to 230 | °C | |
| Nozzle temperature | 210 to 240 | °C | |
| Processing (melt) temperature | 210 to 240 | °C | |
| Mold temperature | 40 to 90 | °C | |
| Injection pressure | 29.4 to 118 | MPa | |
| Back pressure | 0.490 to 3.92 | MPa | |
| Screw speed | 40 to 60 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.59 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |