| About |
|---|
| Lupolen 3026 H is an additivated, low density polyethylene with high rigidity. It contains slip agent. It is delivered in pellet form. Foodlaw compliance information about this product can be found in separate product documentation.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Smoothness,Optical performance,Low coefficient of friction |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.927 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 | g/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| film thickness | 0.8-2.4 mil (20-60 µm | ||
| tensile strength | ISO 527-3 | ||
| yield | 13.0 | MPa | ISO 527-2 |
| MD, 50 µ m, blow molded film | 25.0 | MPa | ISO 527-3 |
| TD, 50 µ m, blow molded film | 18.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 50 µ m, blow molded film | 350 | % | ISO 527-3 |
| TD, fracture, 50 µ m, blow molded film | 600 | % | ISO 527-3 |
| Drop hammer impact | |||
| 50 µ m, blow molded film | 110 | g | ASTM D1709 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| A50 | 100 | ℃ | ISO 306/A50 |
| Melting temperature | |||
| DSC | 114 | ℃ | ISO 3146 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | ASTM D2457 | ||
| 20 °, 50 µ m, blow molded film | > 70 | ASTM D2457 | |
| 60 °, 50.0 µ m, blow molded film | > 110 | ASTM D2457 | |
| Haze | |||
| 50 µ m, blow molded film | < 7.0 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Destruction energy | |||
| 50.0 µm | 40.0 | J/cm | DIN 53373 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 51 | ISO 868 | |
| Ball hardness | |||
| H 49/30 | 21.0 | MPa | ISO 2039-1 |
| Tensile modulus | 300 | MPa | ISO 527-2 |
| friction coefficient | |||
| Blown film | < 0.20 | ISO 8295 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 160 to 200 | °C | |
| Notes |
|---|
| 1. DIN 51454 |
| 2. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |