| About |
|---|
| LUPOX GP-2300 is 30% glass reinforced grade which are made up of non-flame retarded grade .&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Good Electrical Properties,Fatigue resistance,Solvent resistance,HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.52 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 250℃，2.16kg | 18 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.20 to 0.80 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.070 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, 3.20 mm | 123 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm | 4.0 | % | ASTM D638 |
| Bending modulus | |||
| 6.40 mm | 7850 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 6.40 mm | 196 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，6.4mm | 69 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 210 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 6.4 mm | 216 | ℃ | ASTM D648 |
| Melting peak temperature | 223 | ℃ | ASTM D3418 |
| Relative temperature index | |||
| Electrical performance | 140 | ℃ | UL 746 |
| Strength mechanical performance | 140 | ℃ | UL 746 |
| Impact mechanical performance | 130 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 1 mm | 28 | kV/mm | ASTM D149 |
| Arc resistance | PLC 5 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 0 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.71 mm | HB | UL 94 | |
| 1.50 mm | HB | UL 94 | |
| 3.30 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 4.0 to 5.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 240 to 255 | °C | |
| Barrel middle temperature | 245 to 255 | °C | |
| Barrel front temperature | 250 to 260 | °C | |
| Nozzle temperature | 250 to 260 | °C | |
| Processing (melt) temperature | 250 to 260 | °C | |
| Mold temperature | 60 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Solution A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |