| LUPOY PC 1201-10 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength.&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good Clarity,High impact resistance,Good stripping performance,Food contact compliance,High Heat Resistance,HB,V-2 |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 10 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| Water absorption rate | ASTM D570 | ||
| 23℃，24hr | 0.15 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.32 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 900 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 无断裂 | ASTM D256 | |
| Dart impact equipped with measuring instruments | |||
| 23℃，3.20 mm，Total Energy | 87.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, annealed, 4.0 mm | 144 | ℃ | |
| 1.8 MPa, unannealed, 4.0 mm | 128 | ℃ | |
| 1.8 MPa, annealed, 4.0 mm | 141 | ℃ | |
| Vicat Softening Temp | 149 | ℃ | ASTM D1525 5 |
| Ball pressure temperature | > 125 | ℃ | IEC 60598-1 |
| Linear coefficient of thermal expansion | |||
| MD：-40~82℃ | 6.8E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 23℃ | 2.0E+17 | ohms·cm | ASTM D257 |
| Dielectric strength | 17 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 60 Hz | 3.00 | ASTM D150 | |
| Dissipation factor | |||
| 60 Hz | 1.0E-3 | ASTM D150 | |
| Compared to the leakage tracing index | |||
| 2.00 mm | 250 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 3.00 mm | HB | ||
| 0.50 mm | V-2 | ||
| 1.60 mm | V-2 | ||
| 2.50 mm | V-2 | ||
| 2.70 mm | V-2 | ||
| Igniting temperature of the hot wire | |||
| 2 mm | 850 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 26 | % | ASTM D2863 |
| Average combustion degree | 3 | cm | ASTM D635 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.586 | ASTM D542 | |
| Transmittance | 89.0 | % | ASTM D1003 |
| Haze | 0.70 to 1.5 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | ||
| M-level | 73 | ||
| R-level | 118 | ||
| Tensile modulus | 2410 | MPa | ASTM D638 |
| tensile strength | ASTM D638 | ||
| Yield, 23 ℃ | 60.0 | MPa | |
| fracture | 71.0 | MPa | |
| Tensile strain | ASTM D638 | ||
| yield | 6.0 | % | |
| fracture | 150 | % | |
| Bending modulus | 2410 | MPa | ASTM D790 |
| bending strength | 96.0 | MPa | ASTM D790 |
| Wear resistance | |||
| Change in Haze | 45 | % | ASTM D1004 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 1000g, 500 cycles, CS-10F Wheel |
| 4. 9.8 mil Notch Depth |
| 5. 11.1 ft/sec |
| 6. Rate A (50°C/h), Loading 2 (50 N) |
| 7. 5 sec |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |