| About |
|---|
| Description Halogen Free Flame Retardant, Heat Resistant, Chemical Resistance, High Impact Application IT/OA Housing and Components (Adaptor)&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | High impact resistance,Flame Characteristics,High Heat Resistance,Solvent resistance |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 15 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.80 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 3.20 mm | 61.8 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm | 100 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm | 2450 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 3.20 mm | 96.1 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃，3.2mm | 120 | J/m | ASTM D256 |
| 23℃，3.2mm | 740 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 6.4 mm | 121 | ℃ | ASTM D648 |
| Vicat Softening Temp | 135 | ℃ | ASTM D1525 5 |
| Relative temperature index | |||
| Electrical performance | 80.0 | ℃ | UL 746 |
| Strength mechanical performance | 80.0 | ℃ | UL 746 |
| Impact mechanical performance | 80.0 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 2.00 mm | V-0 5VB | UL 94 | |
| 1.00 mm | v-2 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 to 100 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | < 0.020 | % | |
| Barrel rear temperature | 270 to 285 | °C | |
| Barrel middle temperature | 275 to 290 | °C | |
| Barrel front temperature | 275 to 290 | °C | |
| Nozzle temperature | 270 to 285 | °C | |
| Processing (melt) temperature | 275 to 290 | °C | |
| Mold temperature | 80 to 100 | °C | |
| Back pressure | 1.96 | MPa | |
| Screw speed | 40 to 80 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |