| About |
|---|
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Heat Resistance, Good |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Specific Gravity | 1.13 | ISO 1183 | |
| Molding shrinkage | |||
| flow | 0.5-0.8 | % | ISO 294-4 |
| cross-flow | 0.5-0.8 | % | ISO 294-4 |
| Melt Flow Rate | |||
| 260℃，5kg | 23 | g/10min | ISO 1133 |
| Water Absorption | |||
| 23℃，50% r.h. | 0.2 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Strength | |||
| Yield yld | 51 | MPa | ISO 527-2 |
| Broken BRK | 48 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield yld | 4.6 | % | ISO 527-2 |
| Broken BRK | 93 | % | ISO 527-2 |
| Tensile Modulus | 2200 | MPa | ISO 527 |
| Flexural Strength | 83 | MPa | ISO 178 |
| Flexural Modulus | 2260 | MPa | ISO 178 |
| Rockwell hardness | 119 | R Scale | ISO 2039-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod Notched Impact strength | |||
| 23℃ | 50 | KJ/m² | ISO 180/1A |
| -30℃ | 42 | KJ/m² | ISO 180/1A |
| -40℃ | 40 | KJ/m² | ISO 180/1A |
| Charpy Notched Impact Strength | |||
| 23℃ | 48 | kJ/m² | ISO 179 |
| -30℃ | 35 | kJ/m² | ISO 179 |
| -40℃ | 41 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 0.45 MPa | 126 | ℃ | ISO 75-1/-2 |
| 1.80 MPa | 99 | ℃ | ISO 75-1/-2 |
| Vicat Softening Temperature | 121 | ℃ | ISO 306/B |
| Coeff. of linear thermal expansion | |||
| -30℃-80℃ | 8.6E-5 | m/m/℃ | ISO 11359-2 |
| -30℃-80℃ | 8.5E-5 | m/m/℃ | ISO 11359-2 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface Resistivity | 1E15 | ohm | IEC 60093 |
| Volume Resistance | 1E15 | ohm·m | IEC 60093 |
| Dielectric Constant | 2.8 | ASTM D150 | |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 80-100 | ℃ | |
| Drying Time | 4-6 | hr | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 240-270 | ℃ | |
| Rear Temperature Zone 1 | 240-270 | ℃ | |
| Middle Temperature Zone 2 | 245-275 | ℃ | |
| Front Temperature Zone 3 | 245-275 | ℃ | |
| Nozzle temperature | 245-275 | ℃ | |
| Mold Temperature | 50-70 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |