| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 250℃，2.16 kg | 6 | g/10min | ISO 1133 |
| Molding Shrinkage | |||
| flow ，3.2 mm | 0.5-0.7 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Strength | |||
| 49 | MPa | ASTM D638 | |
| 46 | MPa | ISO 527-2 | |
| Elongation at Break | |||
| 90 | % | ASTM D638 | |
| 110 | % | ISO 527-1,2 | |
| Flexural Modulus | |||
| 3.2 mm | 1960 | MPa | ASTM D790 |
| 1870 | MPa | ISO 178 | |
| Flexural Strength | |||
| 3.2 mm | 74.5 | MPa | ASTM D790 |
| 73 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy notched Impact strength | |||
| -30℃ | 13 | kJ/m² | ISO 179/1eA |
| 23℃ | 43 | kJ/m² | ISO 179/1eA |
| Izod Notched Impact strength | |||
| -30℃ | 150 | J/m | ISO 180/1A |
| 23℃ | 490 | J/m | ISO 180/1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| HDT | |||
| 1.8 MPa | 109 | ℃ | ASTM D648 |
| 1.8 MPa | 100 | ℃ | ISO 75-1/-2 |
| Vicat Softening Temperature | 122 | ℃ | ISO 306/B |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 80-100 | ℃ | |
| Drying Time | 4-6 | hr | |
| Maximum Moisture Content | 0.02 | % | |
| Rear Temperature -Zone 1 | 240-270 | ℃ | |
| Middle Temperature -Zone 2 | 245-275 | ℃ | |
| Front Temperature -Zone 3 | 245-275 | ℃ | |
| Nozzle Temperature | 245-275 | ℃ | |
| Melt Temperature | 240-275 | ℃ | |
| Mold Temperature | 50-70 | ℃ | |
| Screw Speed | 40-70 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |