| Description Weather Resistance, Good Flow Application Automotive Exterior |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | ASA+PC |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good liquidity |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 42 | g/10min | ISO 1133 |
| Shrinkage rate | 0.50 to 0.80 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile stress (yield) | 51.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 40 | % | ISO 527-2/50 |
| Bending modulus | 2300 | MPa | ISO 178 |
| Bending stress | 78.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 10 | kJ/m² | |
| 23℃ | 37 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 92.0 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | 108 | ℃ | ISO 306/B50 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 80 to 100 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Temperature at the rear of the barrel | 240 to 270 | °C | |
| Temperature in the middle of the barrel | 245 to 275 | °C | |
| Front temperature of material barrel | 245 to 275 | °C | |
| Nozzle temperature | 245 to 275 | °C | |
| Processing (melt) temperature | 240 to 270 | °C | |
| Mold temperature | 50 to 70 | °C | |
| Screw speed | 40 to 70 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |