| About |
|---|
| Description General Purpose, High Impact, Halogen Free Flame Retardent Application IT/OA(Notebook PC Housing)&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance,Halogen free,Flame Characteristics,V-2,V-0 |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.18 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 250℃，2.16kg | 15 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 to 0.60 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 3.20 mm | 61.3 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm | > 60 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm | 2600 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 3.20 mm | 95.1 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 590 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 6.4 mm | 92.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 97.0 | ℃ | ASTM D1525 4 |
| Relative temperature index | |||
| Electrical performance | 60.0 | ℃ | UL 746 |
| Strength mechanical performance | 60.0 | ℃ | UL 746 |
| Impact mechanical performance | 60.0 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.90 mm | V-2 | UL 94 | |
| 1.00 mm | V-0 | UL 94 | |
| Flammability level | IEC 60695-11-10, -20 | ||
| 1.0 mm，ALL | V-0 | IEC 60695-11-10, -20 | |
| 0.9 mm，ALL | V-2 | IEC 60695-11-10, -20 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 220 to 255 | °C | |
| Barrel middle temperature | 220 to 275 | °C | |
| Barrel front temperature | 245 to 275 | °C | |
| Nozzle temperature | 245 to 275 | °C | |
| Processing (melt) temperature | 245 to 275 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Back pressure | 0.981 to 1.96 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.39 in/min |
| 4. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |