| About |
|---|
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Specific Gravity | 1.18 | ASTM D792 | |
| Molding Shrinkage | |||
| flow | 0.4-0.6 | % | ASTM D955 |
| cross-flow | 0.4-0.6 | % | ASTM D955 |
| Melt Flow Rate | |||
| 250℃，2.16 kg | 14 | g/10min | ASTM D1238 |
| Water Absorption | |||
| 23℃，50% r.h. | 0.2 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Strength | |||
| yld | 590 | kg/cm² | ASTM D638 |
| brk | 590 | kg/cm² | ASTM D638 |
| Tensile Elongation | |||
| yld | 3.8 | % | ASTM D638 |
| brk | 80 | % | ASTM D638 |
| Tensile Modulus | 24370 | kg/cm² | ASTM D638 |
| Flexural Strength | 990 | kg/cm² | ASTM D790 |
| Flexural Modulus | 25000 | kg/cm² | ASTM D790 |
| Rockwell Hardness | 113 | R Scale | ASTM D-785 |
| Shore hardness | – | Shore A | ASTM D2240 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod Notched Impact strength | |||
| 3.2 mm，23℃ | 55 | kgf·cm/cm | ASTM D256 |
| 3.2 mm，-30℃ | 12 | kgf·cm/cm | ASTM D256 |
| 3.2 mm，23℃ | 42 | kgf·cm/cm | ASTM D256 |
| 3.2 mm，-30℃ | 12 | kgf·cm/cm | ASTM D256 |
| 3.2 mm，-40℃ | 11 | kgf·cm/cm | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | – | ℃ | ASTM D3418 |
| HDT | |||
| 4.6kgf | 86 | ℃ | ASTM D648 |
| 18.6kgf | 83 | ℃ | ASTM D648 |
| Vicat Softening Temperature | 91 | ℃ | ASTM D1525 |
| Coeff.of linear therm expansion | |||
| Flow，-30℃-80℃ | 7.2E-7 | m/m/℃ | ASTM D696 |
| Cross-flow，-30℃-80℃ | 7.9E-7 | m/m/℃ | ASTM D696 |
| Thermal Conductivity | |||
| In-plane | – | W/m/K | ASTM E1461 |
| Through-plane | – | W/m/K | ASTM E1461 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 1.5 mm | V-0 | calss | UL 94 |
| 1.5 mm | 5VA | calss | UL 94 |
| 1.2 mm | V-1 | calss | UL 94 |
| Relative Temperature Index | |||
| Electrical，1.2 mm | 60 | ℃ | UL746B |
| Mechanical With Impact，1.2 mm | 60 | ℃ | UL746B |
| Mechanical Without Impact，1.2 mm | 60 | ℃ | UL746B |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Comparative Tracking Index | 2 | PLC Code | UL 746 |
| Surface Resistivity | 1E15 | ohm | ASTM D257 |
| Volume Resistivity | 1E15 | ohm·m | ASTM D257 |
| Dielectric Constant | 2.8 | ASTM D150 | |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 75-85 | ℃ | |
| Drying Time | 3-5 | hr | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 235-265 | ℃ | |
| Rear Temperature -Zone 1 | 220-240 | ℃ | |
| Middle Temperature -Zone 2 | 235-255 | ℃ | |
| Front Temperature -Zone 3 | 250-265 | ℃ | |
| Nozzle Temperature | 250-265 | ℃ | |
| Mold Temperature | 50-80 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |