Lupoy® GN5008HF

About
Description Halogen Free Flame Retardent, High Flow, High Impact Application E&E(OA, Nevigation Housing)&&

Product Description
SupplierLG Chemical
GenericPC+ABS
Material StatusCommercial: Active
FeaturesHigh impact resistance,High liquidity,Halogen free,Flame Characteristics,V-0
AvailabilitysNorth America,Latin America,Asia Pacific,Europe
Process MethodsInjection Molding

Technical Data
PHYSICALNominal valueUnitTest method
Density1.18g/cm³ASTM D792
Melt Flow Rate
250℃,2.16kg18g/10minASTM D1238
Shrinkage rate
MD:3.2 mm0.40 to 0.60%ASTM D955

IMPACTNominal valueUnitTest method
Impact strength of cantilever beam notch
23℃,3.2mm340J/mASTM D256

THERMALNominal valueUnitTest method
Hot deformation temperature
0.45 MPa, unannealed, 6.4 mm88.0ASTM D648
Relative temperature index
Electrical performance60.0UL 746
Strength mechanical performance60.0UL 746
Impact mechanical performance60.0UL 746

FLAME CHARACTERISTICSNominal valueUnitTest method
Flame retardant level UL 94
2.50 mmV-0 UL 94
3.00 mmV-0 UL 94

MECHANICALNominal valueUnitTest method
tensile strength
Yield, 3.20 mm58.8MPaASTM D638
Tensile strain
Fracture, 3.20 mm50%ASTM D638
Bending modulus
3.20 mm2450MPaASTM D790
bending strength
Yield, 3.20 mm84.3MPaASTM D790
Rockwell hardness
R-level113 ASTM D785

Process Conditions
injectionNominal valueUnitTest method
Drying temperature75 to 85°C
Drying time3.0 to 5.0hr
Recommended maximum moisture content< 0.020%
Barrel rear temperature220 to 240°C
Barrel middle temperature235 to 255°C
Barrel front temperature250 to 265°C
Nozzle temperature250 to 265°C
Processing (melt) temperature235 to 265°C
Mold temperature50 to 80°C
Back pressure0.0196 to 0.0588MPa
Screw speed40 to 70rpm

Notes
1. Typical properties: these are not to be construed as specifications.
2. 2.0 in/min
3. 0.39 in/min
4. 4.6kg
【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.