| About |
|---|
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Glass fiber reinforced,Halogen free,Flame Characteristics |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.25 | ASTM D792 | |
| Shrinkage rate | |||
| 3.2mm | 0.1~0.3 | % | ASTM D955 |
| Melt Flow Rate | |||
| 250℃，2.16kg | 10.5 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield 5mm/min | 780 | kg/cm² | ASTM D638 |
| bending strength | |||
| 1.3mm/min | 1200 | kg/cm² | ASTM D790 |
| Bending modulus | |||
| 1.3mm/min | 39000 | kg/cm² | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃-30℃ | 7.5 | kg·cm/cm | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 6.44mm, unannealed | 93 | ℃ | ASTM D648 |
| Flammability | |||
| 1.5mm | V0 | UL94 | |
| Relative temperature index | |||
| Electrical characteristics | 60 | ℃ | UL-746B |
| Mechanical impact performance | 60 | ℃ | UL-746B |
| Non mechanical impact performance | 60 | ℃ | UL-746B |
| Process Conditions | |||
|---|---|---|---|
| Injection molding | Nominal value | Unit | Test method |
| drying temperature | 85~90 | ℃ | |
| Drying time | 4 ~ 5 | hrs | |
| Minimum moisture content | 0.04 | % | |
| Melt Temperature | 240 ~ 265 | ℃ | |
| Nozzle temperature | 245 ~ 255 | ℃ | |
| Forming temperature | 65 ~ 85 | ℃ | |
| Back pressure | 10 ~ 20 | kg/cm² | |
| Screw speed | 40 ~ 70 | rpm | |
| Temperature at the rear of the barrel | 230~240 | ℃ | |
| Temperature in the middle of the barrel | 240~250 | ℃ | |
| Front temperature of material barrel | 245~265 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |