| About |
|---|
| Description General Purpose, High Flow Application Miscellaneous Goods&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | High liquidity |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ASTM D792 |
| Density | 1.13 | g/cm³ | ISO 1183-2 |
| Melt Flow Rate | |||
| 250℃，2.16kg | 6.0 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 260℃，5 kg | 20.5 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD: 3.2 mm, injection molded | 0.50 to 0.80 | % | ASTM D955 |
| Water absorption rate | |||
| saturated | 0.14 | % | ISO 62-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 47.8 | kJ/m² | ISO 179/1eA 2 |
| -30℃ | 18.0 | kJ/m² | ISO 179/1eA 2 |
| Charpy impact strength | |||
| 23℃ | No Break | ISO 179/1eU 2 | |
| -30℃ | No Break | ISO 179/1eU 2 | |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30 ℃, 3.2mm, injection molding | 290 | J/m | ASTM D256 |
| 23 ℃, 3.2mm, injection molding | 570 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm, injection molded | 114 | ℃ | ASTM D648 |
| 1.8 MPa | 109 | ℃ | ISO 75-2 2 |
| Glass transition temperature | 140 | ℃ | ISO 11357-2 2 |
| Vicat Softening Temp | |||
| B50 | 129 | ℃ | ISO 306 2 |
| Linear coefficient of thermal expansion | |||
| TD | 8.9E-5 | 1/℃ | ISO 11359-2 2 |
| MD | 8.2E-5 | 1/℃ | ISO 11359-2 2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 2 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 2 |
| Dielectric strength | 48 | kV/mm | IEC 60243-1 2 |
| Relative permittivity | |||
| 1 MHz | 2.80 | IEC 60250 2 | |
| Dissipation factor | |||
| 1 MHz | 0.010 | IEC 60250 2 | |
| Compared to the leakage tracing index | |||
| CTI | 275 | IEC 60112 2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2000 | MPa | ISO 527-2 2 |
| tensile strength | |||
| Yield, 3.20 mm, injection molding | 55.9 | MPa | ASTM D638 |
| yield | 55.0 | MPa | ISO 527-2 2 |
| Tensile strain | |||
| Fracture, injection molding | > 100 | % | ASTM D638 |
| yield | 5.5 | % | ISO 527-2 2 |
| Nominal strain at break | > 50 | % | ISO 527-2 2 |
| Bending modulus | |||
| 3.20 mm, injection molded | 2260 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm | 90.2 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 114 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 100 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | < 0.020 | % | |
| Barrel rear temperature | 240 to 270 | °C | |
| Barrel middle temperature | 245 to 275 | °C | |
| Barrel front temperature | 245 to 275 | °C | |
| Nozzle temperature | 245 to 275 | °C | |
| Processing (melt) temperature | 240 to 270 | °C | |
| Mold temperature | 50 to 70 | °C | |
| Screw speed | 40 to 70 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3. 2.0 in/min |
| 4. 0.39 in/min |
| 5. 18 °F/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |