| About |
|---|
| Lupoy® GP5300是一种聚碳酸酯+丙烯腈丁二烯苯乙烯(PC+ABS)材料,含有的填充物为30% 玻璃纤维增强材料。 该产品在北美洲、拉丁美洲、欧洲或亚太地区有供货,加工方式为:注射成型。 典型应用领域包括: 房屋 汽车行业&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.33 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：2.0 mm | 0.20 | % | ASTM D995 |
| Melt Flow Rate | |||
| 250℃，2.16kg | 1.5 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 111 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 1.5 | % | ASTM D638 |
| bending strength | |||
| 23℃ | 167 | MPa | ASTM D790 |
| Bending modulus | |||
| 23℃ | 7550 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 117 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50mm | HB | UL-94 | |
| 3.20mm | HB | UL-94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 88 | J/m | ASTM D256 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 70 -80 | °C | |
| Drying time | 5.0-7.0 | Hr | |
| Water content | 0.02 | % | |
| Injection temperature | |||
| Rear barrel temperature | 280-310 | °C | |
| Central temperature of the barrel | 270-310 | °C | |
| Barrel front temperature | 270-310 | °C | |
| Die temperature | 270-310 | °C | |
| Mold temperature | 60-80 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |