| About |
|---|
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Material Status | Commercial: Active |
| Features | High impact resistance,High liquidity |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| 3.2 mm | 0.4~0.7 | % | ASTM D995 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 40 | g/10min | ASTM D1238 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 80 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 85 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| B50 | 90 | ℃ | ASTM D1525 |
| Relative temperature index | |||
| Electrical performance | 60 | ℃ | UL 746B |
| Mechanical impact characteristics | 60 | ℃ | UL 746B |
| Non mechanical impact performance | 60 | ℃ | UL 746B |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| HB | UL 94 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | 1 | V | ICE 60112 |
| Arc resistance | |||
| 23℃ | 6 | ohm.cm | ASTM D495 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，6.4mm | 245 | ASTM D256 | |
| -30℃，6.4mm | 117.6 | ASTM D256 | |
| 23℃，3.2mm | 245 | ASTM D256 | |
| -30℃，3.2mm | 117.6 | ASTM D256 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 107 | R 级 | ASTM D785 |
| tensile strength | |||
| 44 | MPa | ASTM D638 | |
| Tensile strain | |||
| Fracture, 50 mm/min | 30 | % | ASTM D638 |
| bending strength | |||
| 10 mm/min | 59.841 | MPa | ASTM D790 |
| Bending modulus | |||
| 10 mm/min | 1962 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 80 | °C | |
| Drying time | 2~4 | Hr | |
| Moisture content | 0.01 | % | |
| Melting temperature | 210-240 | °C | |
| Injection temperature | |||
| Temperature at the rear of the screw barrel | 180-200 | °C | |
| Temperature in the middle of the screw barrel | 190-210 | °C | |
| Front temperature of screw barrel | 200-210 | °C | |
| Mold head temperature | 200-220 | °C | |
| Mold temperature | 40-70 | °C | |
| Back pressure | 10-30 | bar | |
| Screw speed | 30-60 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |