| About |
|---|
| Description General Purpose, High Impact, Good Coloring, Chemical Resistance Application Mobile Phone Housing&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | High impact resistance,Solvent resistance,Good coloring,HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 12 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.80 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃，3.2mm | 290 | J/m | ASTM D256 |
| 23℃，3.2mm | 690 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 6.4 mm | 130 | ℃ | ASTM D648 |
| Relative temperature index | |||
| Electrical performance | 80.0 | ℃ | UL 746 |
| Strength mechanical performance | 80.0 | ℃ | UL 746 |
| Impact mechanical performance | 80.0 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.70 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 3.20 mm | 56.9 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm | 130 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm | 2160 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 3.20 mm | 88.3 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 117 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 100 to 110 | °C | |
| Drying time | 3.0 to 5.0 | hr | |
| Recommended maximum moisture content | < 0.020 | % | |
| Temperature at the rear of the barrel | 275 to 290 | °C | |
| Temperature in the middle of the barrel | 285 to 305 | °C | |
| Front temperature of material barrel | 290 to 310 | °C | |
| Nozzle temperature | 285 to 305 | °C | |
| Processing (melt) temperature | 290 to 310 | °C | |
| Mold temperature | 80 to 110 | °C | |
| Back pressure | 0.981 to 3.92 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |