| 注塑成型，中等黏度，透明 |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good Clarity |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.2 | ASTM D792 | |
| Shrinkage rate | |||
| 3.2 mm | 0.5 ~ 0.7 | % | ASTM D955 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 8 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 3.2mm, yield 50mm/min | 550 | kg/cm 2 | ASTM D638 |
| Tensile strain | |||
| Yield, 3.20 mm, 50 mm/min | % | ASTM D638 | |
| Fracture, 3.20 mm, 50 mm/min | 100 | % | ASTM D638 |
| bending strength | |||
| 10 mm/min，3.20 mm | 83.385 | MPa | ASTM D790 |
| Bending modulus | |||
| 10 mm/min，3.20 mm | 2060.1 | MPa | ASTM D790 |
| Rockwell hardness | 118 | ASTM D785 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| Unannealed, 6.4 mm | |||
| 18.6kg | 128 | ℃ | ASTM D648 |
| 4.6kg | ℃ | ASTM D648 | |
| Vicat Softening Temp | |||
| B50 | 141 | ℃ | ASTM D1525 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| transparency | 89 | % | ASTM D1003 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 686 | ASTM D256 | |
| -30℃，3.2mm | ASTM D256 |
| Process Conditions | |||
|---|---|---|---|
| Processing conditions | Nominal value | Unit | Test method |
| Drying temperature | 100~ 200 | ℃ | |
| Drying time | 3~ 5 | hrs | |
| Maximum water content | 0.02 | % | |
| Melt temperature | 300 ~ 320 | ℃ | |
| Barrel temperature | |||
| Front section | 300~ 320 | ℃ | |
| Middle section | 280~ 300 | ℃ | |
| Posterior segment | 260 ~ 280 | ℃ | |
| Nozzle temperature | 300 ~ 320 | ℃ | |
| Mold temperature | 80 ~ 120 | ℃ | |
| Back pressure | 10 ~ 40 | kg/cm 2 | |
| Screw speed | 40 ~ 70 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |