| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | SAN |
| Material Status | Commercial: Active |
| Features | Good Clarity |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Volume Rate | 23 | cm³/10min | ISO 1133 |
| Density | 1.08 | g/cm³ | ISO 1183 |
| Shrinkage rate | 0.3-0.4 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃ | 68 | MPa | ISO 527 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.2 | % | ISO 527 |
| Tensile modulus | 3700 | MPa | ISO 527 |
| bending strength | 111 | MPa | ISO 178 |
| Bending modulus | 3800 | MPa | ISO 178 |
| Rockwell hardness | |||
| R-level | 126 | ISO 2039-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 2 | kJ/m² | ISO 180/A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| B120 | 104 | ℃ | ASTM D1525 |
| Hot deformation temperature | |||
| Annealing, 1.80 MPa | 101 | ℃ | ISO 75 |
| Annealing, 0.45MPa | 103 | ℃ | ISO 75 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | 87-88 | % | ASTM D1003 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |