| About |
|---|
| Description High temperature, Non-Halogen Flame Retardant Application Electric&Electronic parts&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | PPA |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics,High Heat Resistance |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.42 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 1.4 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, 3.20 mm | 155 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm | 2.5 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm | 10300 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm | 225 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 90 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 285 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 23℃ | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 23 ℃，1 mm | 23 | kV/mm | ASTM D149 |
| Compared to the leakage tracing index | |||
| Solution A | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.45 mm | V-0 | ||
| 0.80 mm | V-0 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 to 120 | °C | |
| Drying time | 4.0 to 5.0 | hr | |
| Recommended maximum moisture content | 0.060 to 0.10 | % | |
| Barrel rear temperature | 300 to 320 | °C | |
| Barrel middle temperature | 310 to 330 | °C | |
| Barrel front temperature | 310 to 330 | °C | |
| Nozzle temperature | 320 to 340 | °C | |
| Processing (melt) temperature | 320 to 330 | °C | |
| Mold temperature | 100 to 140 | °C | |
| Back pressure | 14.7 to 29.4 | MPa | |
| Screw speed | 50 to 150 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 24 Hr |
| 3. 0.20 in/min |
| 4. 0.051 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |