| About |
|---|
| LUTENE BB0808 is mainly intended for the extrusion of blown film with high mechanical property for the manufacture of shrink film and pallet shrink covers. LUTENE BB0808 have the balanced shrink properties and good clarity make suitable for shrink film. LUTENE BB0808 contains neither slip agent nor antiblock agent. Applications: Shrinkage film, Pallet shrink cover, chopping board, All types of industrial packing.&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Good Clarity |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.921 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.80 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| F50 | > 500 | hr | ASTM D1693 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tear resistance | ASTM D1922 | ||
| MD | 27.5 | MPa | ASTM D1922 |
| TD | 27.5 | MPa | ASTM D1922 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| tensile strength | ASTM D882 | ||
| MD, fracture | 21.6 | MPa | ASTM D882 |
| TD, fracture | 20.6 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture | 550 | % | ASTM D882 |
| TD, fracture | 650 | % | ASTM D882 |
| Drop hammer impact | 220 | g | ASTM D1709 |
| Oxygen permeability | 2000 | cm³/m²/24 hr | Internal Method |
| Water vapor permeability | 12 | g/m²/24 hr | Internal Method |
| Nitrogen transfer rate | 3500 | cm³/m²/24 hr | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 94.0 | ℃ | ASTM D1525 |
| Melting temperature | 110 | ℃ | DSC |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60° | 80 | ASTM D2457 | |
| Haze | 8.0 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 160 to 190 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |