| Description LUTENE-H BE0350 is a HDPE material with high parison stability and good processing properties. BE0350 can be used to produced containers for wide range of applications. Applications LUTENE-H BE0350 is used to produce for the following parts. lightweight container from 2 to 10 liters in capacity from 1 to 30 liters in capacity for Jerrican pipes and sheets&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good liquidity,High impact resistance,Good Rigidity,Excellent Processability,High density |
| Availabilitys | Latin America,Europe,North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.958 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 190℃，2.16kg | 0.25 | g/10min | ASTM D1238 |
| 190℃，21.6kg | 20 | g/10min | ASTM D1238 |
| 190℃，5kg | 1.1 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| F50 | 40.0 | hr | ASTM D1693 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod Notched Impact strength | 440 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa, unannealed | 76.0 | ℃ | ASTM D648 |
| Vicat softening point | 127 | ℃ | ASTM D1525 2 |
| Melting temperature | 134 | ℃ | DSC |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 64 | ASTM D2240 | |
| Tensile Strength | |||
| Yield yld | 30 | MPa | ASTM D638 |
| Tensile Strain | |||
| Broken BRK | > 500 | % | ASTM D638 |
| Flexural Modulus | 1200 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion Molded | Nominal value | Unit | Test method |
| Joint temperature | 175 to 190 | °C | |
| Melt Temperature | 180 | °C | |
| Die Temperature | 160 to 190 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |