Lutene® LB5000

About
LUTENE LB5000 is mainly intended for extrusion coating and can be processed uniform thickness and width. LUTENE LB5000 is also noted for the excellent heat stability and has good silicone coating processibility. LB5000 has a good adhesion strength with paper and paper board and excellent neck-in characteristic. LUTENE LB5000 contains no additives. Agency Ratings: USA FDA 21CRF 117.1520(c) Japaness Ministry of Health and Welfare Notification No. 20 Standard Applications: Flexible package (Tie layer or sealant layer of laminating film) Paper and paperboard coating (Release paper, paper cup, kraft paper)&&

About

LUTENE LB5000 is mainly intended for extrusion coating and can be processed uniform thickness and width. LUTENE LB5000 is also noted for the excellent heat stability and has good silicone coating processibility. LB5000 has a good adhesion strength with paper and paper board and excellent neck-in characteristic. LUTENE LB5000 contains no additives. Agency Ratings: USA FDA 21CRF 117.1520(c) Japaness Ministry of Health and Welfare Notification No. 20 Standard Applications: Flexible package (Tie layer or sealant layer of laminating film) Paper and paperboard coating (Release paper, paper cup, kraft paper)&&

Product Description
Supplier	LG Chemical
Generic	LDPE
Material Status	Commercial: Active
Features	Excellent Processability,Low shrinkage,Good bond
Availabilitys	North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.918	g/cm³	ASTM D1505
Melt Flow Rate
190℃，2.16kg	5.0	g/10min	ASTM D1238

film	Nominal value	Unit	Test method
Initial sealing temperature	110	℃
Water vapor permeability	20	g/m²/24 hr	Internal Method

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	83.0	℃	ASTM D1525
Melting temperature	107	℃	DSC

Supplementary information	Nominal value	Unit	Test method
Adhesion to Aluminum	392.3	N/m	Internal Method

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D, molded	43		ASTM D2240
tensile strength			ASTM D638
Yield, molding	8.83	MPa	ASTM D638
Fracture, molded	11.8	MPa	ASTM D638
Tensile strain
Fracture, molded	550	%	ASTM D638
Bending modulus
Compression Molding	196	MPa	ASTM D790

Process Conditions
Extrusion	Nominal value	Unit	Test method
Shrinkage 4	20.0	mm
Minimum coating weight 5	13	g/m²

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.