| LUVOCOM® 1105-7310是一种聚醚醚酮(PEEK)材料,含有的填充物为玻璃纤维增强材料。 该产品在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货,。 LUVOCOM® 1105-7310的主要特性有: 阻燃/额定火焰 Flame Retardant 具可灭菌性 抗翘曲 良好的尺寸稳定性 典型应用领域包括: 纺织/纤维 工程/工业配件 航空航天 汽车行业 医疗/保健&& |
| Product Description | |
|---|---|
| Supplier | Lehmann |
| Generic | PEEK |
| Material Status | Commercial: Active |
| Features | Low warping,Good Dimensional Stability,Steam sterilized,Hydrolysis stability,Good liquidity,Flame Characteristics,High Heat Resistance,Solvent resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.52 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD | 0.9 | % | ISO 294-4 |
| MD | 0.4 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，24hr | <=0.1 | % | ISO 62 |
| Melt Flow Rate | |||
| 380℃，5.0kg | 11 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 85 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.5 | % | ISO 527-2 |
| bending strength | |||
| 3.20% strain, 23 ℃ | 125 | MPa | ISO 178 |
| Bending modulus | |||
| 23℃ | 5000 | MPa | ISO 178 |
| Elastic modulus | |||
| 23℃ | 6000 | MPa |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| A50 | 325 | ℃ | ISO 306/A50 |
| Maximum operating temperature | |||
| In the air, continuous | 250 | ℃ | |
| In the air, for a short period of time | 260 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | |||
| 10V | >=1.0E+12 | Ω.cm |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | – | V-0 | UL-94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 40 | kJ/m² | ISO 179/1eU |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80-150 | °C | |
| Drying time | 2.0-6.0 | Hr | |
| Recommended moisture content | <=0.20 | % | |
| Barrel rear temperature | 320-380 | °C | |
| Barrel middle temperature | 330-390 | °C | |
| Barrel front temperature | 340-400 | °C | |
| Nozzle temperature | 350-410 | °C | |
| Mold temperature | 80-160 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |