| LUVOCOM® 1105-7373是一种聚醚醚酮(PEEK)材料,含有的填充物为碳纤维增强材料。 该产品在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货,。 LUVOCOM® 1105-7373的主要特性有: Flame Retardant 良好的尺寸稳定性 良好的刚度 耐化学品 耐磨 典型应用领域包括: 工程/工业配件 纺织/纤维 航空航天 汽车行业 医疗/保健&& |
| Product Description | |
|---|---|
| Supplier | Lehmann |
| Generic | PEEK |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,Hydrolysis stability,Low coefficient of friction,Flame Characteristics,High Heat Resistance,Lubricating,Good wear resistance,Solvent resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.62 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 380℃，10 kg | 12.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | 0.30 to 0.60 | % | DIN 16901 |
| Water absorption rate | |||
| 23℃，24hr | < 0.10 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 13000 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 145 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 1.8 | % | ISO 527-2 |
| Bending modulus | 11000 | MPa | ISO 178 |
| bending strength | 200 | MPa | ISO 178 |
| friction coefficient | |||
| dynamic | 0.14 | ||
| static state | 0.12 | ||
| Bending strain | 2.3 | % | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| -30℃ | 30 | kJ/m² | ISO 179/1fU |
| 23℃ | 32 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 260 | ℃ | ISO 75-2/A |
| Continuous use temperature | 250 | ℃ | UL 746B |
| Maximum operating temperature | |||
| short-term | 270 | ℃ | |
| Vicat Softening Temp | 320 | ℃ | ISO 306/A |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| insulation resistance | > 1.0E+5 | ohms | IEC 60167 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | |||
| Hot air dryer, A | 150 | °C | |
| Hot air dryer, B | 120 | °C | |
| Drying time | |||
| Hot air dryer, A | 3.0 to 6.0 | hr | |
| Hot air dryer, B | 6.0 to 8.0 | hr | |
| Recommended maximum moisture content | 0.050 | % | |
| Barrel rear temperature | 360 to 370 | °C | |
| Barrel middle temperature | 380 to 390 | °C | |
| Barrel front temperature | 390 to 400 | °C | |
| Nozzle temperature | 360 to 380 | °C | |
| Processing (melt) temperature | 390 | °C | |
| Mold temperature | 170 to 190 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |