| Product Description | |
|---|---|
| Supplier | Lehmann |
| Material Status | Commercial: Active |
| Features | Soft,Agglomerability,Block Copolymer |
| Availabilitys | Africa & Middle East ,North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.46 | g/cm³ | ISO 1183 |
| Molding shrinkage | |||
| MD | 0.9 | % | ISO 294-4 |
| TD | 1.5 | % | ISO 294-4 |
| Water Absorption | |||
| 23℃，24hr | <=0.1 | % | ISO 62 |
| Melt Flow Rate | |||
| 380℃，10.0kg | 15 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Strength | |||
| 23℃ | 85 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Broken BRK, 23 ℃ | 3.5 | % | ISO 527-2 |
| Flexural Strength | |||
| 4.70% strain, 23 ℃ | 125 | MPa | ISO 178 |
| Flexural Modulus | |||
| 23℃ | 3500 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Coeff. of linear thermal expansion | |||
| Maximum operating temperature | 250 | ℃ | |
| Maximum operating temperature | 260 | ℃ |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Dissipation Factor | |||
| Volumetric resistance | >=1.0E+12 | Ω.cm | |
| Surface resistance | >=1.0E+12 | Ω.cm |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| – | V-0 | UL 94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 40 | kJ/m² | ISO 179/1eU |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 120 -150 | °C | |
| Drying Time | 3-8 | Hr | |
| Drying Temperature | |||
| Rear Temperature Zone 1 | 360-370 | °C | |
| Middle Temperature Zone 2 | 380-390 | °C | |
| Front Temperature Zone 3 | 390-400 | °C | |
| Die Temperature | 360-380 | °C | |
| Mold Temperature | 170-190 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |