LUVOCOM® 1114-9752

About
LUVOCOM® 1114-9752 is a Polyetherketoneketone (PEKK) material filled with carbon fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of LUVOCOM® 1114-9752 are: Conductive ESD Protection Heat Resistant Lubricated Wear Resistant Typical applications include: Aerospace Automotive Engineering/Industrial Parts Fabrics/Fibers Medical/Healthcare&&

About

LUVOCOM® 1114-9752 is a Polyetherketoneketone (PEKK) material filled with carbon fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of LUVOCOM® 1114-9752 are: Conductive ESD Protection Heat Resistant Lubricated Wear Resistant Typical applications include: Aerospace Automotive Engineering/Industrial Parts Fabrics/Fibers Medical/Healthcare&&

Product Description
Supplier	Lehmann
Generic	PEKK
Material Status	Commercial: Active
Features	Conductive,Low coefficient of friction,Electrostatic discharge protection,High Heat Resistance,Lubricating,Good wear resistance
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.59	g/cm³	ISO 1183
Melt Volume Rate
380℃，10 kg	15.0	cm³/10min	ISO 1133
Shrinkage rate
3.0 mm	0.10 to 0.30	%	DIN 16901
Water absorption rate
23℃，24hr	< 0.10	%

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	18000	MPa	ISO 527-2
tensile strength
fracture	170	MPa	ISO 527-2
Tensile strain
yield	1.4	%	ISO 527-2
Bending modulus	16000	MPa	ISO 178
bending strength	265	MPa	ISO 178
Bending strain	1.7	%	ISO 178

IMPACT	Nominal value	Unit
Charpy Unnotch Impact strength
-30℃	25	kJ/m²
23℃	30	kJ/m²

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	305	℃	ISO 75-2/A
Continuous use temperature	270	℃	UL 746B
Linear coefficient of thermal expansion
MD	5.0E-6	1/℃	DIN 53752

Electrical performance	Nominal value	Unit	Test method
Surface resistivity	< 1.0E+4	ohms	IEC 60093
insulation resistance	< 1.0E+5	ohms	IEC 60167

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature
Hot air dryer, A	150	°C
Hot air dryer, B	120	°C
Drying time
Hot air dryer, A	4.0 to 6.0	hr
Hot air dryer, B	6.0 to 10	hr
Barrel rear temperature	370 to 420	°C
Barrel middle temperature	380 to 420	°C
Barrel front temperature	390 to 420	°C
Nozzle temperature	390 to 420	°C
Processing (melt) temperature	390	°C
Mold temperature	210 to 230	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.