| About |
|---|
| LUVOCOM® 1115-8559是一种聚醚酮酮 (PEKK)材料,含有的填充物为碳纤维增强材料。 该产品在欧洲、非洲和中东、北美洲、拉丁美洲或亚太地区有供货,。 LUVOCOM® 1115-8559的主要特性有: Flame Retardant 水解稳定性 耐化学品 耐磨 良好的刚度 LUVOCOM® 1115-8559的典型应用领域为:工程/工业配件&& |
| Product Description | |
|---|---|
| Supplier | Lehmann |
| Generic | PEKK |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Hydrolysis stability,Low coefficient of friction,Flame Characteristics,Self-lubricating,Lubricating,Good wear resistance,Solvent resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.51 | g/cm³ | ISO 1183 |
| Shrinkage rate | 0.30 to 0.60 | % | DIN 16901 |
| Water absorption rate | |||
| 23℃，24hr | < 0.10 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 14000 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 165 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 1.5 | % | ISO 527-2 |
| Bending modulus | 11000 | MPa | ISO 178 |
| bending strength | 225 | MPa | ISO 178 |
| Bending strain | 2.0 | % | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 30 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Continuous use temperature | 260 | ℃ | UL 746B |
| Maximum operating temperature | |||
| short-term | 300 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | < 1.0E+8 | ohms | IEC 60093 |
| insulation resistance | < 1.0E+9 | ohms | IEC 60167 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | |||
| Hot air dryer, A | 140 | °C | |
| Hot air dryer, B | 150 | °C | |
| Drying time | |||
| Hot air dryer, A | 4.0 to 6.0 | hr | |
| Hot air dryer, B | 4.0 to 8.0 | hr | |
| Barrel rear temperature | 370 to 390 | °C | |
| Barrel middle temperature | 380 to 420 | °C | |
| Barrel front temperature | 390 to 420 | °C | |
| Nozzle temperature | 390 to 420 | °C | |
| Processing (melt) temperature | 390 | °C | |
| Mold temperature | 180 to 220 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |