| LUVOCOM® 19-8094 VP是一种聚酰胺 46（尼龙 46）材料,含有的填充物为碳纤维增强材料。 该产品在亚太地区、北美洲、拉丁美洲、欧洲或非洲和中东有供货,。 LUVOCOM® 19-8094 VP的主要特性有: 传导性 润滑 良好的刚度 典型应用领域包括: 工程/工业配件 商业/办公用品 汽车行业 纺织/纤维&& |
| Product Description | |
|---|---|
| Supplier | Lehmann |
| Generic | PA 46 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Conductive,Lubricating |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.34 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 300℃，2.16kg | 12 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 300℃，2.16 kg | 13.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | 0.30 to 0.60 | % | DIN 16901 |
| Water absorption rate | |||
| 23℃，24hr | < 1.0 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 11000 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 165 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 2.2 | % | ISO 527-2 |
| Bending modulus | 9000 | MPa | ISO 178 |
| bending strength | 235 | MPa | ISO 178 |
| Bending strain | 2.6 | % | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 40 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | > 290 | ℃ | ISO 75-2/A |
| Continuous use temperature | 150 | ℃ | UL 746B |
| Maximum operating temperature | |||
| short-term | 160 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | < 1.0E+6 | ohms | IEC 60093 |
| insulation resistance | < 1.0E+6 | ohms | IEC 60167 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | |||
| Hot air dryer, A | 80 | °C | |
| Vacuum dryer, B | 80 | °C | |
| Drying time | |||
| Hot air dryer, A | 2.0 to 8.0 | hr | |
| Vacuum dryer, B | 2.0 to 12 | hr | |
| Barrel rear temperature | 285 to 315 | °C | |
| Barrel middle temperature | 305 to 315 | °C | |
| Barrel front temperature | 305 to 315 | °C | |
| Nozzle temperature | 280 to 330 | °C | |
| Processing (melt) temperature | 310 | °C | |
| Mold temperature | 90 to 130 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |